| 膜片开关银浆固化后变色失效分析 |
| The Discoloration Failure Analysis after Curing on Membrane Switch Silver Slurry |
| 投稿时间：2016-05-16 |
| DOI： |
| 中文关键词: 金属材料 膜片开关 银浆 银线变色断线 失效 |
| 英文关键词: metallic materials membrane switch Silver paste silver line discoloration break failure |
| 基金项目:云南省科技创新强省项目(2014AA020 柔性线路板用高性能高可靠环保导电银浆开发与产业化)。 |
|
| 摘要点击次数: 2319 |
| 全文下载次数: 3298 |
| 中文摘要: |
| 针对膜片开关银浆固化后偶尔出现的银线变色断线现象进行分析。通过电镜观察，推测失效原因在于膜片开关生产封装过程中引入的有机物污染腐蚀银线路，从而出现银线变色断线，导致线路失效。 |
| 英文摘要: |
| Color break phenomenon analysis of membrane switch paste after curing occasional silver wire. By electron microscopy, it was inferred that the reason for the failure of the membrane switch production and packaging process introduced organic pollution corrosion silver line, which appears discolored silver wire breakage, resulting in line failure. |
|