某微细粒砷黄铁矿包裹金矿的非氰浸出研究 |
Study on Non-cyanide Extraction for a Ore Micro-fine Gold Enclosed by Arsenopyrite |
投稿时间:2018-12-13 |
DOI: |
中文关键词: 有色金属冶金 难浸金矿 非氰浸出 边磨边浸 预氧化 |
英文关键词: nonferrous metallurgy refractory gold ore non-cyanide leaching leaching-grinding pre-oxidation |
基金项目:国家自然科学基金项目(51574146) |
|
摘要点击次数: 2502 |
全文下载次数: 1854 |
中文摘要: |
采用非氰浸化剂(石硫合剂)对含金为2.47 g/t的甘肃某微细粒砷黄铁矿包裹金矿进行浸出试验,研究预处理方式和浸出工艺对金浸出率的影响。结果表明,石硫合剂对金的直接搅拌浸出率低于30%,该矿属难浸金矿石;采用边磨边浸-搅拌浸出的方式,浸出率可提升至68.4%;增加碱式预氧化处理,可将金的浸出率进一步提升到80%以上。采用最优的工艺,边磨边碱式预氧化36 h,经石硫合剂搅拌浸出5 h,金的浸出率可达到91.5%。 |
英文摘要: |
The effect of pre-oxidation and leaching technology on leaching rate of gold was studied by using lime sulfur agent as extraction agent to leach a micro-arsenopyrite coated gold ore with a gold content of 2.47 g/t in Gansu province. The results showed that direct agitation leaching rate of gold was less to 30% by lime sulfur agent. The ore was refractory gold ore. The leaching rate of gold was improved to 68.4% by stirring-grinding-leaching method. The extraction rate of gold was enhanced to over 80% by adding alkaline pre-oxidation treatment. The leaching rate of gold was 91.5% by alkaline pre-oxidation for 36 h and grinding-leaching for 5 h using lime sulfur agent. |
查看全文
查看/发表评论 下载PDF阅读器 |
关闭 |