| Ir和IrRh40合金的组织结构与性能研究 |
| Study on Microstructure and Properties of Ir and IrRh40 Alloy |
| 投稿时间：2016-04-12 |
| DOI： |
| 中文关键词: 金属材料 Ir IrRh40 组织结构 性能 |
| 英文关键词: metal materials Ir IrRh40 structure properties |
| 基金项目:国家自然科学基金(51361014)、稀贵金属综合利用国家重点实验室开放课题(SKL-SPM-201527)、云南省重点项目(2016FA053) |
|
| 摘要点击次数: 2253 |
| 全文下载次数: 2624 |
| 中文摘要: |
| 用光学显微镜和扫描电镜对尺寸为Φ6 mm的加工态Ir和IrRh40合金棒材的金相组织、高温氧化后的组织和IrRh40/GH3128合金焊缝进行了研究；采用力学试验机对IrRh40/GH3128的焊接强度进行了研究。结果表明，Rh的加入在Ir中能起到了明显的细化晶粒作用，显著提高了Ir的抗氧化性能；IrRh40与GH3128合金的焊接性能良好，焊缝强度可达到474 MPa。 |
| 英文摘要: |
| Microstructure of processing state, microstructure after high temperature oxidation of Ir and IrRh40 alloy bar with 6 mm were investigated by means of optical microscope (OM), scanning electron microscope (SEM); the weld fracture and welding strength of IrRh40/GH3128 alloy were studied by OM, SEM and tensile testing machine. The results indicate that addition of Rh play a significant role in refining the grain size of Ir. The oxidation resistance of Ir is improved by addition of Rh .The welding performance of IrRh40 and GH3128 alloy is good. Tension strength of the weld line can reach 474 MPa. |
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |