| 表面活性剂对Ag-10Pd复合粉形貌的影响 |
| Effect of Surfactants on the Shape of Ag-10Pd Composited Powder |
| Received:January 26, 2013 |
| DOI： |
| 中文关键词: 金属材料 银钯粉 电子浆料 表面活性剂 制备 |
| 英文关键词: metal materials silver-palladium powder electronic paste surfactant preparation |
| 基金项目:国家自然科学基金(51261008)、国家支撑计划项目(2012BAE06B00)、昆明贵金属研究所R&D项目(2012020603)。 |
| Author Name | Affiliation | E-mail | | CHEN Liqiao | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-platinum Metals Co. Ltd., Kunming 650106, China | chenlq118@126.com | | LI Shihong | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-platinum Metals Co. Ltd., Kunming 650106, China | | | JIN Wuhui | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-platinum Metals Co. Ltd., Kunming 650106, China | | | XIONG Qingfeng | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-platinum Metals Co. Ltd., Kunming 650106, China | | | LIU Jisong | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-platinum Metals Co. Ltd., Kunming 650106, China | | | HUANG Fuchun | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-platinum Metals Co. Ltd., Kunming 650106, China | | | LUO Hui | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-platinum Metals Co. Ltd., Kunming 650106, China | | | WANG Ke | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-platinum Metals Co. Ltd., Kunming 650106, China | |
|
| Hits: 4970 |
| Download times: 4299 |
| 中文摘要: |
| 银钯浆料具有较好焊接性与抗银迁移能力及可调的烧结温度，使得银钯复合粉在厚膜微电子浆料中占有重要的地位。采用水合肼作为还原剂，通过表面活性剂种类的选择、加入方式的改变及加入量的控制，制备了不同形貌的Ag-10Pd复合粉。结果表明，聚乙烯吡咯烷酮对制备单分散的多面体银钯复合粉有较好的作用，而明胶的加入可以获得较好的球形复合粉，对其加入方式与加入量进行调控，可以选择性制备不同粒径与形态的Ag-10Pd复合粉。 |
| 英文摘要: |
| Silver-palladium paste has a very important position in the fields of thick film microelectronic pastes due to its good weldability, resistance to silver migration and adjustable sintering temperature. In this paper, by using hydrazine hydrate as a reducing agent, Ag-10Pd composited powder of different shapes was prepared through the selection of surfactants, the variation of the addition methods and the control of the amount of surfactants. The experimental results showed that polyvinylpyrrolidone had a good effect on synthesizing monodisperse polyhedral silver-palladium powder, while by the addition of gelatin, the spherical composited powder could be obtained. The particle sizes and shapes of Ag-10Pd powder could also be regulated and controlled by different addition methods and the addition amount of gelatin, respectively. |
|