含金硫酸渣硫酸盐化焙烧-氯化浸金研究 |
Processing of Gold-containing Slag from Sulfuric Acid Production Using Sulfatizing Roasting Followed by Chlorine Leaching |
Received:August 17, 2013 |
DOI: |
中文关键词: 冶金技术 含金硫酸渣 氯盐浸出 浸出率 |
英文关键词: metallurgy gold-containing slag from sulfuric acid production chlorine leaching leaching rate |
基金项目: |
Author Name | Affiliation | E-mail | YOU Dahai | College of Resources and Environmental Engineering, Wuhan University of Technology, Wuhan 430070, China | ydh0015@126.com | ZHANG Yahui | College of Resources and Environmental Engineering, Wuhan University of Technology, Wuhan 430070, China | yahui.zhang@whut.edu.cn | LONG Gang | Zhongkuang Gold Industry Co.Ltd., Zhaoyuan 265401, Shandong, China | | TU Bo | College of Resources and Environmental Engineering, Wuhan University of Technology, Wuhan 430070, China | | HUANG Junwei | College of Resources and Environmental Engineering, Wuhan University of Technology, Wuhan 430070, China | |
|
Hits: 4458 |
Download times: 4766 |
中文摘要: |
针对难处理含金硫酸渣进行了硫酸盐化焙烧-氯化(氯酸钠-氯盐)浸出试验研究,考察了氯酸钠用量、氯化钠用量、液固比、浸出时间、浸出温度、焙烧预处理等因素对金浸出率的影响。研究结果表明,在优化的试验条件:氯化钠用量为80 kg/t,氯酸钠100 kg/t,反应温度80℃,液固比为3,反应时间为4 h下,处理该含金硫酸渣可以得到91.44%的金浸出率。 |
英文摘要: |
Sulfatizing roasting and chlorine leaching of refractory gold-containing slag from sulfuric acid production have been investigated. The effects of sodium chlorate dosage, sodium chloride dosage, liquid-solid ratio, leaching time, reaction temperature and pretreatment condition on leaching recovery of gold have been studied. The results show that the leaching rate can reach as high as 91.44% under the optimum conditions that the addition of NaClO3 is 100 kg/t, the addition of NaCl is 80 kg/t, the liquid-solid ratio is 3, the leaching temperature is 80℃ and the leaching time is 4.0 h. |