| Ag-O系定向凝固制备藕状多孔Ag |
| Fabrication of Lotus-type Porous Silver with Directional Solidification of Ag-O System |
| Received:June 20, 2014 |
| DOI： |
| 中文关键词: 藕状多孔Ag 氧气压力 气孔率 平均气孔直径 |
| 英文关键词: lotus-type porous silver oxygen pressure porosity average pore diameter |
| 基金项目:稀贵金属综合利用新技术国家重点实验室开放课题。 |
| Author Name | Affiliation | E-mail | | LIANG Juan | School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China | | | YANG Tianwu | School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China | | | LI Zaijiu | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Kunming Institute of Precious Metals, Kunming 650106, China | | | XIE Ming | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Kunming Institute of Precious Metals, Kunming 650106, China | | | JIN Qinglin | School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China | jinqinglin@yahoo.com |
|
| Hits: 3661 |
| Download times: 3963 |
| 中文摘要: |
| 金属-气体共晶定向凝固(Gasar)是一种制备藕状多孔金属的新工艺，在高压纯氧气氛中，利用自行研制的Gasar模铸装置制备了藕状多孔Ag试样，并研究了氧气压力对气孔率、平均气孔直径的影响。结果表明:在多孔Ag中，氧气压力对气孔率和平均气孔直径的影响十分显著。随着氧气压力的增加，气孔率增大，而平均气孔直径减少，当氧气压力为0.5 MPa时，气孔分布最为均匀。 |
| 英文摘要: |
| Directional solidification of metal/gas eutectic (Gasar) is a novel process for fabricating porous metals with pores parallel to the solidification direction. By use of the developed ‘Gasar’ apparatus, lotus-type porous silver samples have been fabricated in pressurized oxygen. At the same time, the effects of gas pressure on porosity, pore nucleation, pore size and distribution were studied. The results show that oxygen pressure has great influence on pore morphology. The porosity increases with increasing pressure of oxygen. The average pore diameter decreases with increasing of oxygen pressure. |
|