| 退火温度对AgCuIn/QSn复合焊料界面影响 |
| The Influence of Annealing Temperature on the AgCuIn/QSn Composite Brazing Composite |
| Received:August 13, 2014 |
| DOI： |
| 中文关键词: 复合材料 复合 退火 界面 |
| 英文关键词: composite material composite annealing interface |
| 基金项目: |
| Author Name | Affiliation | | MAO Duan | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-Platinum Metals Co. Ltd., Kunming 650106, China | | WANG Jian | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-Platinum Metals Co. Ltd., Kunming 650106, China | | WU Qingwei | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-Platinum Metals Co. Ltd., Kunming 650106, China | | CHEN Wen | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-Platinum Metals Co. Ltd., Kunming 650106, China | | WANG Guangqing | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-Platinum Metals Co. Ltd., Kunming 650106, China | | CHEN Guohua | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-Platinum Metals Co. Ltd., Kunming 650106, China | | LI Linxiu | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Sino-Platinum Metals Co. Ltd., Kunming 650106, China |
|
| Hits: 3816 |
| Download times: 3826 |
| 中文摘要: |
| 采用室温固相复合技术制备AgCuIn/QSn复合焊料，选用不同退火温度对AgCuIn/QSn复合焊料进行扩散退火，利用拉力试验机、扫描电子显微镜考察热处理温度对AgCuIn/QSn复合焊料界面的影响。结果表明，退火工艺为550℃/6 h时复合界面结合效果最佳。 |
| 英文摘要: |
| The AgCuIn/QSn composite brazing was made by room temperature solid phase composite technology, and annealed at different heat treatment temperatures. The influence of annealing temperature on the AgCuIn/QSn composite brazing composite interface was studied by tensile testing instrument and scanning electron microscopy. The results showed that the best composite interface was got at 550℃/ 6 h annealing. |
|