| 汽车后挡风玻璃加热线银浆的烧结工艺研究 |
| Study on the Sintering process of Silver Paste on Auto Rear Glass Hot Wires |
| Received:August 29, 2015 |
| DOI： |
| 中文关键词: 加热线 银浆 烧结工艺 |
| 英文关键词: hot wires silver paste sintering process |
| 基金项目:国家自然科学基金(51262017；51362017)、稀贵金属先进材料协同创新中心协同创新基金(14051708)、稀贵金属综合利用新技术国家重点实验室开放基金(No.SKL-SPM-201502)。 |
| Author Name | Affiliation | E-mail | | YAN Jikang | Faculty of Materials Science and Engineering, Kunming University of Science and Technology,Key Laboratory of Advanced Materials of Precious-Nonferrous Metals, Ministry of Education, Key Laboratory of Advanced Materials of Yunnan Province, Kunming Key Laboratory of Advanced Materials of Precious-Nonferrous Metals, Kunming 650093, China | scjk@sina.com | | TengYuan | Faculty of Materials Science and Engineering, Kunming University of Science and Technology,Key Laboratory of Advanced Materials of Precious-Nonferrous Metals, Ministry of Education, Key Laboratory of Advanced Materials of Yunnan Province, Kunming Key Laboratory of Advanced Materials of Precious-Nonferrous Metals, Kunming 650093, China | | | YAN Fangcun | Faculty of Materials Science and Engineering, Kunming University of Science and Technology,Key Laboratory of Advanced Materials of Precious-Nonferrous Metals, Ministry of Education, Key Laboratory of Advanced Materials of Yunnan Province, Kunming Key Laboratory of Advanced Materials of Precious-Nonferrous Metals, Kunming 650093, China | | | LI Wenlin | Sino-Platinum Metals Co.Ltd., Kunming 650156, China | | | DU Jinghong | Faculty of Materials Science and Engineering, Kunming University of Science and Technology,Key Laboratory of Advanced Materials of Precious-Nonferrous Metals, Ministry of Education, Key Laboratory of Advanced Materials of Yunnan Province, Kunming Key Laboratory of Advanced Materials of Precious-Nonferrous Metals, Kunming 650093, China | | | GAN Guoyou | Faculty of Materials Science and Engineering, Kunming University of Science and Technology,Key Laboratory of Advanced Materials of Precious-Nonferrous Metals, Ministry of Education, Key Laboratory of Advanced Materials of Yunnan Province, Kunming Key Laboratory of Advanced Materials of Precious-Nonferrous Metals, Kunming 650093, China | | | YI Jianhong | Faculty of Materials Science and Engineering, Kunming University of Science and Technology,Key Laboratory of Advanced Materials of Precious-Nonferrous Metals, Ministry of Education, Key Laboratory of Advanced Materials of Yunnan Province, Kunming Key Laboratory of Advanced Materials of Precious-Nonferrous Metals, Kunming 650093, China | |
|
| Hits: 3990 |
| Download times: 4995 |
| 中文摘要: |
| 以球形银粉、无铅玻璃粉和有机载体为原料制备汽车后挡风玻璃加热线用银浆。通过不同的烧结工艺，利用SEM观察烧结银膜的形貌，测试烧结膜的方阻及附着力，讨论烧结温度、保温时间对银膜性能的影响。结果表明，烧结温度640℃时，能获得性能较好的银膜，银膜附着力为9N，银膜方阻为20 mΩ/□；保温时间7 min时，能获性能较好的银膜，银膜附着力为9.6 N，银膜方阻为17.2 mΩ/□。 |
| 英文摘要: |
| Silver paste for auto rear glass hot wires was prepared with the mixture of spherical silver powder, lead-free glass frit and organic vehicle. With different sintering process, the effects of sintering tempertature and sintering time on properties of Ag film were discussed by observing the morphology of the sintered Ag film with SEM and measuring the resistivity and adhesion. The results show that silver film with good performance can be obtained with the sintering temperature at 640℃, silver film adhesion for 9 N, silver film resistivity for 20 mΩ/□;silver film with good performance can be obtained with the sintering time at 7 min, silver film adhesion for 9.6 N, silver film resistivity for 17.2mΩ/□. |
|