| 一步生长合成具有催化活性的银花状球 |
| One-Step Synthesis of Flower-like Silver Sphere with Catalytic Activity |
| Received:April 19, 2017 |
| DOI： |
| 中文关键词: 纳米材料 银 花状球结构 生长机制 催化活性 |
| 英文关键词: nano material silver flower-like sphere structures growth mechanism catalytic activity |
| 基金项目:国家自然科学基金(21363011)、云南省面上项目(2013FB094)、云南省院所技术开发专项项目(2013DC033)。 |
| Author Name | Affiliation | E-mail | | MENG Xianwei | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Kunming Institute of Precious Metals, Kunming 650106, China | mxwd163yx@163.com | | CHAO Yunxiu | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Kunming Institute of Precious Metals, Kunming 650106, China | | | GUO Shuailong | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Kunming Institute of Precious Metals, Kunming 650106, China | | | LI Yuxiu | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Kunming Institute of Precious Metals, Kunming 650106, China | | | HU Changyi | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Kunming Institute of Precious Metals, Kunming 650106, China | | | YANG Hongwei | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Kunming Institute of Precious Metals, Kunming 650106, China | yhw@ipm.com.cn | | FENG Qingfu | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Kunming Institute of Precious Metals, Kunming 650106, China | | | LI Yanqiong | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Kunming Institute of Precious Metals, Kunming 650106, China | | | CUI Hao | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Kunming Institute of Precious Metals, Kunming 650106, China | | | CHEN Jialin | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,Kunming Institute of Precious Metals, Kunming 650106, China | |
|
| Hits: 2632 |
| Download times: 2399 |
| 中文摘要: |
| 通过改变加入硝酸的量在水溶液中一步生长合成银花状球。采用扫描电镜、X射线衍射、紫外可见吸收光谱对其进行分析表征。结果表明，所制得的银花状球结构由交错的微纳米片构成，且花状球结构的平均直径可在400 nm~1.5 μm之间调节。研究发现，加入酸的量对产物的尺寸和形貌有决定性作用并基于此提出其生成机理。对比实验表明，银花状球对对硝基苯酚和硼氢化钠的反应具有催化活性，速率常数为369.8 s-1.g-1。 |
| 英文摘要: |
| Flower-like Ag sphere structure was synthesized via a one-step reaction in aqueous solution by changing the amount of nitric acid added, and characterized by scanning electron microscope (SEM), X-ray diffraction (XRD) and ultraviolet-visible (UV-Vis) spectroscopy. The results showed that the product was composed of staggered silver nanoplates and the average diameter could be adjusted accurately from 400 nm to 1.5 μm. The amount of nitric acid had crucial effect on the size and morphology of the flower-like Ag sphere structure and accordingly a plausible formation mechanism was proposed. Contrast experiments revealed that flower-like Ag sphere diaplayed catalytic activity in the reaction of p-nitrophenol with sodium borohydride at a rate constant of 369.8 s-1.g-1. |
|