| 铜捕集法从失效汽车催化剂中回收铂、钯和铑的研究 |
| Recovery of Pt, Pd and Rh from Spent Auto Catalysts by Copper Collection Method |
| Received:December 27, 2017 |
| DOI： |
| 中文关键词: 有色金属冶金 铂族金属 铜捕集法 失效汽车催化剂 回收 |
| 英文关键词: non-ferrous metallurgy platinum group metal? copper collection method? spent auto catalyst? recovery |
| 基金项目:国家自然科学基金项目(51504106)；云南省科技计划项目(2015DC001、2015FB204、2017FA030)。 |
| Author Name | Affiliation | E-mail | | ZHAO Jiachun | Kunming Institute of Precious Metals, State key Laboratory of Advanced Technology of ComprehensiveUtilization of Platinum Metals, Sino-platinum Metals Co. Ltd., Kunming 650106, China | zhaojiacuhn@ipm.com.cn | | CUI Hao | Kunming Institute of Precious Metals, State key Laboratory of Advanced Technology of ComprehensiveUtilization of Platinum Metals, Sino-platinum Metals Co. Ltd., Kunming 650106, China | | | BAO Simin | Kunming Institute of Precious Metals, State key Laboratory of Advanced Technology of ComprehensiveUtilization of Platinum Metals, Sino-platinum Metals Co. Ltd., Kunming 650106, China | | | TONG Weifeng | Kunming Institute of Precious Metals, State key Laboratory of Advanced Technology of ComprehensiveUtilization of Platinum Metals, Sino-platinum Metals Co. Ltd., Kunming 650106, China | | | DONG Haigang | Kunming Institute of Precious Metals, State key Laboratory of Advanced Technology of ComprehensiveUtilization of Platinum Metals, Sino-platinum Metals Co. Ltd., Kunming 650106, China | donghaigang0404@126.com |
|
| Hits: 2996 |
| Download times: 3091 |
| 中文摘要: |
| 采用铜捕集法从失效汽车催化剂中回收铂族金属，重点研究了CaO/SiO2质量比、捕集剂、熔炼温度和时间、以及还原剂对Pt、Pd和Rh回收率的影响。结果表明，在CaO/SiO2=1.05，CuO配比35%~40%，还原剂配比6%，熔炼温度1400℃，熔炼时间5 h的条件下，Pt、Pd和Rh回收率分别为98.2%、99.2%和97.6%。 |
| 英文摘要: |
| A copper collection method was used to recover platinum group metals from a spent auto catalysts. The influences of CaO/SiO2 weight ratio, collection agent and reductant on Pt, Pd and Rh recoveries were studied. The recovery rates are 98.2%, 99.2% and 97.6% for Pt, Pd and Rh, respectively, when the collection condition is as follows: 1.05 of CaO/SiO2 weight ratio, 35%~40% of CuO ratio, 6% of reductant ratio, 1400℃ of smelting temperature and 5 h of smelting time. |
|