| 热老化对Pd/Al2O3选择性催化NH3反应性能的影响 |
| Effect of Thermal Ageing of Pd/Al2O3 Catalyst on the Selectivity of NH3 Formation |
| Received:May 16, 2019 |
| DOI： |
| 中文关键词: Pd/Al2O3催化剂 热老化 NH3生成 三效催化反应(TWC) Pd颗粒 |
| 英文关键词: Pd/Al2O3 catalyst thermal ageing NH3 formation three-way catalytic reactions(TWC) Pd particle |
| 基金项目:国家自然科学基金(51676017, 21862010)、云南省科技人才和平台计划项目(2018IC091)、云南省重大科技专项(2018ZE017) |
| Author Name | Affiliation | E-mail | | YAO Li-peng | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Kunming Institute of Precious Metals, Kunming 650106, China | ylpppp@163.com | | WANG Cheng-xiong | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Kunming Institute of Precious Metals, Kunming 650106, China
State-Local Joint Engineering Laboratory of Precious Metal Catalytic Technology and Application, Kunming Sino-platinum Metals Catalysts Co.Ltd., Kunming 650106, China | | | TAN Jian-wei | School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China | | | REN De-zhi | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Kunming Institute of Precious Metals, Kunming 650106, China | | | ZHENG Ting-ting | State-Local Joint Engineering Laboratory of Precious Metal Catalytic Technology and Application, Kunming Sino-platinum Metals Catalysts Co.Ltd., Kunming 650106, China | | | ZHAO Yun-kun | State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Kunming Institute of Precious Metals, Kunming 650106, China
State-Local Joint Engineering Laboratory of Precious Metal Catalytic Technology and Application, Kunming Sino-platinum Metals Catalysts Co.Ltd., Kunming 650106, China | yk.zhao@spmcatalyst.com |
|
| Hits: 2936 |
| Download times: 2223 |
| 中文摘要: |
| 研究了在三效催化反应过程中热老化对Pd/Al2O3选择性催化NH3反应性能的影响。在稀/富循环流中进行稳态实验，采用X射线衍射(XRD)、BET比表面积、X射线光电子能谱(XPS)、拉曼光谱(Raman)和透射电镜(TEM)对催化剂的物理化学性质进行表征。结果表明，高温热老化导致活性金属钯的分散度降低、颗粒尺寸增大、Pd2+活性物种的相对比例下降，这些微结构变化促使催化剂的三效活性降低、氨选择性增加。热老化诱导催化剂表面活性钯颗粒明显增大，较大的钯颗粒有助于NO解离生成活性氮物种，进而与氢反应生成NH3。 |
| 英文摘要: |
| The effect of thermal aging on the selectivity of NH3 products in three-way catalytic reaction was studied. Steady-state experiments were carried out in dilute/rich circulating flow. X-ray diffraction (XRD), BET specific surface area, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy (Raman) and transmission electron microscopy (TEM) were used to characterize the physicochemical properties of the catalysts. The results showed that high temperature aging led to a decrease in the dispersion of palladium, an increase in particle size and a decrease in the relative proportion of the Pd2+ active species. These microstructural changes contribute to the reduction of the three-way activity of catalysts, resulting in the increase in ammonia selectivity. Thermal ageing induces a significant increase in active palladium particles on the catalyst surface, and larger particles promotes NO to dissociate to form active nitrogen species, which in turn react with hydrogen to form NH3. |
|