| 亚硫酸钠浸出-甲醛还原回收氯化渣中的银 |
| Recovery of Silver in Chloride Residue by Sodium Sulfite Leaching-Formaldehyde Reduction Process |
| Received:June 14, 2019 |
| DOI： |
| 中文关键词: 氰化金泥 氯化渣 银精炼 亚硫酸钠浸出 甲醛还原 |
| 英文关键词: cyanide gold mud chlorinated residue silver refining sodium sulfite leaching formaldehyde reduction |
| 基金项目:陕西省渭南市科技计划项目(2015TCZX-22) |
| Author Name | Affiliation | E-mail | | WANG Xian-zhong | Tongguan Zhongjin Smelting Co.Ltd., Tongguan 714399, Shaanxi, China | 835692250@qq.com | | ZHANG Shao-hui | Tongguan Zhongjin Smelting Co.Ltd., Tongguan 714399, Shaanxi, China | | | GUO Xiao-liang | Tongguan Zhongjin Smelting Co.Ltd., Tongguan 714399, Shaanxi, China | guoxiaoliang1985@126.com | | LÜ Chao-fei | SDIC Jincheng Metallurgy Co.Ltd., Lingbao 472500, Henan, China | | | QIAO Guang-jun | Tongguan Zhongjin Smelting Co.Ltd., Tongguan 714399, Shaanxi, China | | | SONG Zhen-hai | Tongguan Zhongjin Smelting Co.Ltd., Tongguan 714399, Shaanxi, China | | | DONG Wen-long | Tongguan Zhongjin Smelting Co.Ltd., Tongguan 714399, Shaanxi, China | | | Wang，Yong-feng | SDIC Jincheng Metallurgy Co.Ltd., Lingbao 472500, Henan, China | |
|
| Hits: 3181 |
| Download times: 2596 |
| 中文摘要: |
| 为了改善氰化金泥湿法精炼过程中氯化渣铁粉置换工艺熔炼粗银时的工作环境，提高银的回收率，采用亚硫酸钠浸出-甲醛还原方法处理氯化渣。结果表明，在pH=8.5、液固质量比为20:1、35℃的条件下用浓度为250 g/L的亚硫酸钠溶液浸出氯化渣3 h后，银浸出率大于99%；浸银液在40%甲醛与银比例为5:2 (mL/g)、50℃的条件下还原1.5 h，银还原率达99%以上。浸出渣返回金泥氯化分金流程，浸银液还原后可再生循环使用，银综合回收率可达98%以上。 |
| 英文摘要: |
| In order to improve the working environment of smelting coarse silver by the replacement process of iron powder from chloride residue in the wet refining process of cyanide gold mud and the recovery of silver, selective leaching of silver from chlorinated residue and silver reduction with formaldehyde have been investigated. The results showed that the silver leaching ratio of chlorinated residue was over 99% after leaching by 250 g/L sodium sulfite solution with a liquid-solid mass ratio (L/S) of 20:1 for 3 hours at pH 8.5 and 35℃. The leached solution was reduced by formaldehyde with a ratio of 40% formaldehyde to silver of 5:2 (mL/g) for 1.5 h at 50℃, and the silver reduction rate was over 99%. The leached residue was returned to the gold slime chlorination process, and the silver leaching solution could bereuseble, and the comprehensive recovery rateof silver could reach over 98%. |
|