| AgCuNiSi扁丝轧制工艺研究 |
| Study on Rolling Process of AgCuNiSi Flat Wire |
| Received:September 09, 2020 |
| DOI： |
| 中文关键词: AgCuNiSi扁丝 轧制 宽展 显微组织 硬度 |
| 英文关键词: AgCuNiSi flat wire rolling spread microstructure hardness |
| 基金项目:国家重点研发计划(2017YFB0305700)；国家自然科学基金(U1602271, U1602275)；云南省科技计划项目(2018ZE011, 2018ZE012, 2018ZE022, 2018ZE026, 2015IB012, 2016HB026) |
| Author Name | Affiliation | E-mail | | CHEN Yong-tai | Kunming Institute of Precious Metals, State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Sino-Platinum Metals Co.Ltd., Kunming 650106, China
School of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China | cyt@ipm.com.cn.com | | XIE Ming | Kunming Institute of Precious Metals, State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Sino-Platinum Metals Co.Ltd., Kunming 650106, China | powder@ipm.com.cn | | CHEN Li | Kunming Institute of Precious Metals, State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Sino-Platinum Metals Co.Ltd., Kunming 650106, China | | | FANG Ji-heng | Kunming Institute of Precious Metals, State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Sino-Platinum Metals Co.Ltd., Kunming 650106, China | | | HU Jie-qiong | Kunming Institute of Precious Metals, State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Sino-Platinum Metals Co.Ltd., Kunming 650106, China
School of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China | | | YANG You-cai | Kunming Institute of Precious Metals, State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Sino-Platinum Metals Co.Ltd., Kunming 650106, China | | | WANG Sai-bei | Kunming Institute of Precious Metals, State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals, Sino-Platinum Metals Co.Ltd., Kunming 650106, China
School of Material Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China | |
|
| Hits: 1813 |
| Download times: 0 |
| 中文摘要: |
| 对AgCuNiSi合金丝材进行扁丝轧制，研究了AgCuNiSi扁丝轧制过程中宽展行为以及组织与性能的演变。结果表明，轧制法可以获得尺寸波动很小、高精度的扁丝；AgCuNiSi扁丝的宽展量可以用M. Kazeminezhad宽展公式来预测；扁丝轧制过程中对第二相颗粒有破碎和弥散分布作用；随着压下率的增加，硬度分布更加均匀，由不均匀变形逐渐转变为均匀变形。通过压下率的控制，可以获得均匀变形的AgCuNiSi扁丝。 |
| 英文摘要: |
| The width spread, microstructure and properties of AgCuNiSi flat wire during rolling were studied. The results showed that flat wire with small size fluctuation and high precision could be obtained by rolling method. The width spread of AgCuNiSi flat wire could be predicted by M. Kazeminezhad Formula. The second phase particles were broken and dispersed during the rolling process of flat wire. The hardness distribution became more uniform and the deformation changed from non-uniform to uniform gradually with the increase of the reduction rate. The uniform deformation of AgCuNiSi flat wire could be obtained by controlling the reduction rate. Content |
|