| 次氯酸钠浸出贵州难浸金矿的电化学研究 |
| Electrochemical study on the leaching of a refractory gold ore in Guizhou with sodium hypochlorite |
| Received:September 14, 2023 |
| DOI： |
| 中文关键词: 次氯酸钠浸金 电化学 浸出率 难浸金矿 |
| 英文关键词: sodium hypochlorite leaching of gold electrochemistry leaching rate refractory gold ore |
| 基金项目:贵州省科技计划项目(黔科合基础[2019]1412) |
| Author Name | Affiliation | | ZOU Tao | College of Materials and Metallurgy, Guizhou University, Guiyang 550000, China | | TANG Daowen | College of Materials and Metallurgy, Guizhou University, Guiyang 550000, China | | HAN Zhilong | Guizhou Zijin Mining Company Limited, Qianxinan 562205, Guizhou, China | | YUAN Xin | College of Materials and Metallurgy, Guizhou University, Guiyang 550000, China | | XU Caiwu | College of Materials and Metallurgy, Guizhou University, Guiyang 550000, China | | YANG Xiugao | College of Materials and Metallurgy, Guizhou University, Guiyang 550000, China |
|
| Hits: 854 |
| Download times: 454 |
| 中文摘要: |
| 以贵州难浸金矿矿粉作为原料制作矿物碳糊电极，通过浸金体系在不同温度、不同浓度和不同pH的NaClO溶液中进行电化学研究。结果表明，在NaClO浸金体系中，较优浸出条件为，NaClO溶液浓度0.7~0.9 mol/L，浸出温度30~35 ℃，pH=13.5。验证实验表明，在NaClO浓度0.9 mol/L，反应温度为30 ℃，溶液pH=13.5的条件下浸出3 h，金平均浸出率为93.38%。 |
| 英文摘要: |
| The mineral carbon paste electrode was prepared by using the refractory gold ore powder from Guizhou province as raw material, and the electrochemical study was carried out in a gold leaching system with NaClO solution as the leaching agent under the conditions of different temperatures, different concentrations and different pH values. The results show that the optimal leaching conditions are as follows: 0.7~0.9 mol/LNaClO solution concentration, leaching temperature at 30~35 ℃ and pH=13.5. Typically, an average leaching rate of gold reached 93.38% when the leaching was conducted at 30 ℃ for 3 hours in 0.9 mol/L NaClO solution with a pH value of 13.5. |
|